3m 583 Thermal Bonding Film for FPC and Plastic

• Customization: Available
• Certification: RoHS, ISO9001
• Color: Brown
• Model NO.: 3M 583
• Heat Resistance: High Temperature
• Waterproof: Waterproof
• Application: Plastic, Metal, Leather, Glass, Ceramic
• Adhesive: Hot Melt Adhesive
• Base Material: No Backing
• Type: Double Sided Tape
• Die Cutting: Yes
• OEM: Yes
• Transport Package: Carton
• Specification: 0.05mm x 1219mm x 55m
• Trademark: 3M
• Origin: China
• HS Code: 3919909090
• Production Capacity: 1000 Rolls Per Month
• Package Size: 130.00cm * 30.00cm * 30.00cm
• Package Gross Weight: 20.000kg

Product Description

Product Description

 

3M 583 Brown Hot Melt Adhesive Film Thermal Bonding Film for FPC and Plastic Board Bonding

3M Thermal Bonding Film 583 is a high strength, flexible, nitrile phenolic based thermosetting adhesive film. It can be heat or solvent activated for bonding. It can also be lightly crosslinked using a post heat exposure.This hot melt film adhesive provides a strong, permanent bond to the surface to which it is applied. The adhesive can be used for splicing of glass fabric during PCB board manufacturing. Can be solvent activated in the uncured form.
3M TBF 583 must be stored at or below 4°C (40°F) for maximum storage life. 

 

Feature

* Flexible
* Heat or solvent activation
* Can be die-cut
* Slight surface tack
* Heat crosslinkable option
* Lower temperature lamination of the nitrile phenolic film range

Base Resin	Nitrile phenolic
Adhesive Thickness	2 mil (0.05 mm)
Tack	Slight
Color	Brown
Construction	2 mil adhesive + 3 mil sillicone paper liner
Tensile (psi)	400 (before)   3140 (after)
Elongation (%)	800 (before)  180 (after)
Modulus (psi)	240 (before)  13800 (after)
2 Lb. Dead Load Overlap Shear Heat Resistance	71°C (160°F) (before) >149°C (300°F) (after)

To make a bond, remove the liner and place the adhesive film between the two substrates. The bond is then made through heat and pressure using a heated press, a hot roll laminator, a hot shoe thermode method or similar equipment. Alternatively, the adhesive can be first tacked (lightly bonded) to one of the substrates using low heat, the liner can then be removed and second substrate placed to the exposed adhesive surface, and a bond made using heat and pressure. Since 3M TBF 583 has a slight surface tack, in some cases it may be tacked to a substrate with pressure only (no heat).